| Che. | Resin Properties | Boleng bo tloaelehileng | Yuniti | Mokhoa oa Teko |
| 1 | Matla a Khoheli a khethehileng, 23℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Mold Shrinkage, 23℃, 3.2mm,23℃ | 0.4-0.7 | % | ASTM D955 |
| 3 | Melt Flow Rate, 220 ℃, 10kg | 22 | g/10 mets | ASTM D1238 |
| 4 | Matla a Tensile ho Puno, 23℃, 50mm/min, 3.2mm | 49 | MPa | ASTM D638 |
| 5 | Tensile Elongation at Yield, 23℃, 50mm/min, 3.2mm | 5 | %, (Metsotso) | ASTM D638 |
| 6 | Tensile Elongation nakong ea Phomolo, 23'℃, 50mm/min, 3.2mm | 10 | %, (Metsotso) | ASTM D638 |
| 7 | Tensile Modulus, 23℃, 50mm/min, 3.2mm | 2350 | MPa | ASTM D638 |
| 8 | Matla a Flexural, 23 ℃, 15mm / min, 3.2mm | 78 | MPa | ASTM D790 |
| 9 | Flexural Modulus, 23℃, 15mm/min, 3.2mm | 2550 | MPa | ASTM D790 |
| 10 | Izod Impact Matla, Notched, 3.2mm, 23℃ | 220 | J/m | ASTM D256 |
| 11 | Izod Impact Matla, Notched, 3.2mm, -30℃ | 90 | J/m | ASTM D256 |
| 12 | Izod Impact Matla, Notched, 6.4mm, 23℃ | 220 | J/m | ASTM D256 |
| 13 | Izod Impact Matla, Notched, 6.4mm, -30℃ | 90 | J/m | ASTM D256 |
| 14 | Rockwell Hardness, R-Scale | 110 | / | ASTM D785 |
| 15 | HDT, Edgewise, 1.82MPa, 6.4mm, Ha e na thuso | 85 | °C | ASTM D648 |
| 16 | VICAT, 50N, 50℃/h | 92 | °C | ASTM D1525 |
| 17 | RTI ea Motlakase | 95 | °C | UL 746B |
| 18 | RTI Mechanical e nang le Impact | 95 | °C | UL 746B |
| 19 | RTI Mechanical ntle le Impact | 95 | °C | UL 746B |
| 20 | Ho chesa, 1.5mm | HB | / | UL94 |
| 21 | Ho chesa, 3.0mm | HB | / | UL94 |